連鑄坯縱裂紋和卷渣等缺陷的成因及應(yīng)對措施綜述

吳振剛  王占國  李哲  張濤  梁娟

（河鋼集團唐鋼生產(chǎn)制造部，唐山市濱河路9號）

摘要：文中綜合論述了連鑄坯縱裂、卷渣、氣泡、鉛芯等缺陷的形成機理及影響因素，連鑄坯縱裂受到鋼種成分、結(jié)晶器傳熱、坯殼所受的摩擦力以及凝固溫度等因素影響；連鑄坯卷渣、氣泡和鉛芯所受影響因素相近，與SEN設(shè)計、SEN吹氬流量大小、澆注速度等工藝因素相關(guān)。針對以上鑄坯缺陷，文中從工藝控制、保護渣選用、SEN設(shè)計等角度，給出了相應(yīng)的解決方案供大家探討。

關(guān)鍵詞：連鑄、縱裂紋、卷渣、氣泡

Causes and Countermeasures for longitudinal cracks and slag inclusion in slab

Wu zhengang Wangzhanguo Lizhe Zhangtao Liangjuan

(HBIS grop Tangsteel company, Tangshan, 063000, Hebei, China)

Abstract: The formation mechanism and influencing factors of slag longitudinal crack, slag entrapment, bubble and lead core are discussed comprehensively in this paper. Argon blowing flow rate, pouring speed and other factors related to the process. In view of the above slab defects, this paper gives the corresponding solutions from the aspects of process control, mold flux selection, SEN design and so on.

Keywords: Continuous casting； longitudinal crack; mold power entrapment; bubble

1 前言

隨著鋼鐵工業(yè)的進步，對于連鑄坯的質(zhì)量要求越來越高，連鑄機的裝備水平與技術(shù)的進步為連鑄坯質(zhì)量提供了保證。但是實際生產(chǎn)中，連鑄坯依然會出現(xiàn)各種缺陷。文中針對連鑄坯縱裂、卷渣、氣泡、鉛芯等缺陷的形成機理及影響因素進行了總結(jié)，并針對這些缺陷給出了相應(yīng)的解決方案供大家探討。

2 縱裂紋成因及應(yīng)對措施

2.1包晶鋼對縱裂紋的影響

在澆鑄含碳量為0.08-0.15%的包晶鋼時，縱裂紋的產(chǎn)生是一個非常特殊的問題，它主要出現(xiàn)在結(jié)晶器上部。由于δ鐵素體相和奧氏體相的熱收縮系數(shù)不同，導致凝固坯殼所受熱應(yīng)力有所不同，這是產(chǎn)生縱裂紋的主要原因。坯殼厚度的增加以及厚度不均勻都會導致收縮加劇，在縱向上產(chǎn)生應(yīng)力集中而導致表面裂紋。鋼中的碳含量與坯殼凝固收縮率的關(guān)系如圖1所致。